Home > Products > Aluminum sheet > Aluminum Sheet Alloy 5052

Aluminum Sheet Alloy 5052

Basic Info

Model No.:  5052

Product Description

Model NO.: 5052 Certification: ASTM, JIS, GB/T Grade: 5000 Series Surface Treatment: Mill Finish Sample: Free Shape: Rectangular Specification: SGS, ROHS HS Code: 760612 Application: Decorations Technique: Rolling Temper: O - H112 Alloy: Alloy Type: Aluminum Sheets Trademark: Baodi Origin: China Aluminum sheet, Alloy: 5052
Temper: H32, H34, H112, O
Thickness: 0.5-150mm
Dimension: As per customers' requirements.

Chemical composition:
Aluminum Balance
Chromium 0.15 - 0.35
Copper 0.1 max
Magnesium 2.2 - 2.8
Manganese 0.1 max
Remainder Each 0.05 max
Remainder Total 0.15 max
Silicon + Iron 0.45 max
Zinc 0.1 max

5052 is a non-heat treatable alloy that is weldable. It is hardened by cold work. It has good forming characteristics and good corrosion resistance, including resistance to salt water.

Commonly used in the manufacture of hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, and appliances. Commonly used in sheet metal work and
In sheet metal parts.

Specification Name: 5000 series Aluminum Sheet
Alloy: 5052, 5005, 5754, 5083 etc.
Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.
Thickness: 0.2-200mm
Width: Up to 1800mm
Length: up to 6000mm
Surface treatment: mill finished, PVC coated, Print marks
Feature Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
Forming: It is readily formed at room temperature. Successive cold working decreases the formability.
Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.
Forging: It may be forged in the temperature range of 950 F down to 500 F
Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
Annealing: Anneal at 650 F and air cool.
Hardening: Hardens only from cold working.
Application hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.
Alloy Chemical Component %≤
Si Fe Cu Mn Mg Cr Ni Zn Ti others Al
single total
5052 0.25 0.4 0.1 0.1 2.2-2.8 0.15-0.3 \ 0.1 \ 0.05 0.15 remainder
5005 0.3 0.7 0.2 0.2 0.5-1.1 0.1 \ 0.25 \ 0.05 0.15 remainder
5754 0.4 0.4 0.1 0.5 2.6-3.6 0.3 \ 0.2 0.15 0.05 0.15 remainder
5083 0.4 0.4 0.1 0.4-1.0 4.0-4.9 0.05-0.25 \ 0.25 0.15 0.05 0.15 remainder
Contact Ms. Cherry Xia   Tel: 0086-15106464366

Contact us if you need more details on Aluminium Sheet. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Aluminum Sheet、Aluminium Sheets. If these products fail to match your need, please contact us and we would like to provide relevant information.

Product Categories : Aluminum sheet

Email to this supplier
  • *Subject:
  • To:

  • *Messages:
    Your message must be between 20-8000 characters