Home > Products > Extruded Aluminium Profile > 6082 T6, T651 Solid Aluminum Breadboard Unpolished 12in*24in Price Matt Huge Selection Construction/Decoration/Electronic Products

6082 T6, T651 Solid Aluminum Breadboard Unpolished 12in*24in Price Matt Huge Selection Construction/Decoration/Electronic Products

Basic Info

Model No.:  6082 T6 T651

Product Description

Model NO.: 6082 T6 T651 Application: Decorations Grade: 6000 Series Technique: Rolled Temper: T6,T651, T6,T651 Thickness: 6-300mm Trademark: BAODI Origin: China Type: Aluminum Sheets Shape: Rectangular Surface Treatment: Unpolished Alloy: Alloy Certification: ASTM Size: 1000*2000mm,1220*2440mm,1200*2400mm Specification: GB/T 3880-2006 HS Code: 76061250  Solid aluminum breadboard unpolished 6082 T6,T651

6061

Chemical composition:
Aluminum    Balance   
Copper      0.15 - 0.4
Iron         0 - 0.7
Magnesium   0.8 - 1.2
Manganese   0.15 max
Other       0.15 max
Remainder Each   0.05 max
Silicon       0.4 - 0.8
Titanium     0.15 max
Zinc         0.25 max


Principal Design Features
Probably the most commonly available, heat treatable aluminum alloy.
Applications
Commonly used in the manufacture of heavy-duty structures requiring good corrosion resistance, truck and marine components, railroad cars, furniture, tank fittings, general structural and high pressure applications, wire products, and in pipelines.
Machinability
Machinability in the harder T 4 and T6 tempers is good. It is notably less easy to machine in the annealed temper.
Forming
Easily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are all readily accomplished using standard methods.
Welding
The alloy has very good welding characteristics and may be welded by all of the common welding techniques. Gas tungsten arc welding is generally used for thin sections (less than 0.032") and gas metal arc welding is used for heavier sections. Use alloy 4043 filler wire for best results, although a decrease in T 6 properties will result.
Heat Treatment
Solution heat treat at 990 F for adequate time to allow for thorough heating and then water quench. Precipitation hardening is done at 320 F for 18 hours and air cool, followed by 350 F for 8 hours and air cooling.
Forging
The alloy is capable of being hot forged at temperatures in the range of 900 F to 750 F.
Hot Working
Hot working may be done in the temperature range of 700 F to 500 F.
Cold Working
Cold working in the O temper condition is readily performed. The alloy is notably less easy to cold form in the T 4 and T 6 tempers.
Annealing
Annealing should be done at 775 F for 2 to 3 hours followed by controlled cooling at 50 f per hour down to 500 F, then air cool.
Aging
The aging precipitation heat treatment is done at 350 F for 8 hours followed by air cooling. This produces the T6 temper.
Other Physical Props
Electrical conductivity 40% of copper.
Other Mechanical Props
Shear strength for O temper is 12 ksi and for T 6 temper it is 30, ksi
Physical Data
Density (lb / cu. in.)  0.098
Specific Gravity  2.7
Melting Point (Deg F)  1090
Modulus of Elasticity Tension  10
Modulus of Elasticity Torsion  3.8
 
 

Contact us if you need more details on Solid Aluminum Breadboard. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Unpolished Aluminum、Aluminum. If these products fail to match your need, please contact us and we would like to provide relevant information.

Product Categories : Extruded Aluminium Profile

Email to this supplier
  • *Subject:
  • To:

  • *Messages:
    Your message must be between 20-8000 characters