Factory Price of En Standard 3003/5005/5052/5083 /6061 Aluminum Alloy Sheet /Plate

Basic Info

Model No.:  3003/5005/5052/5083 /6061

Product Description

Model NO.: 3003/5005/5052/5083 /6061 Application: Moulds, Die, Machine Parts Grade: 5000 Series / 6000 Series Technique: Roll Temper: T3 - T8 Sample: Free Specification: SGS, ROHS HS Code: 760612 Type: Aluminum Sheets Shape: Rectangular Surface Treatment: Mill Finish Alloy: Alloy Certification: ASTM, JIS, GB/T Trademark: Baodi Origin: China
Specifications
1)Grade:5052,5754,5083,6061,6082
2)Temper:O,H111,H112,T6,T651


Dimensions and weight can be produced according to clients' specifications.

Surface:
Smooth,no scratch,no roll mark,no black spot,no oil stain, without freckles

Shipment:
Port: NingBo or Qingdao port or according to customers' requirement
Packing: standard packing for ocean shipment, anti-static corrosion.
Lead time: 20 days
 
Specification Name: 6000 series Aluminum sheet
Alloy: 6061, 6082, 6063 etc.
Temper: O, H112, T4, T6, T651 etc.
Thickness: 6-200mm
Width: Up to 1500mm
Surface treatment: mill finished, Print marks
Feature Machinability: In the harder T 4 and T6 tempers it is good. It is notably less easy to machine in the annealed temper.
Forming: Easily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are all readily accomplished using standard methods.
Welding: It has very good welding characteristics and may be welded by all of the common welding techniques.
Heat Treatment: Solution heat treat at 990 F for adequate time to allow for thorough heating and then water quench. Precipitation hardening is done at 320 F for 18 hours and air cool, followed by 350 F for 8 hours and air cooling.
Forging: It is capable of being hot forged at temperatures in the range of 900 F to 750 F.
Hot Working: Hot working may be done in the temperature range of 700 F to 500 F.
Cold Working: Cold working in the O temper condition is readily performed. The alloy is notably less easy to cold form in the T 4 and T 6 tempers.
Annealing: Annealing should be done at 775 F for 2 to 3 hours followed by controlled cooling at 50 f per hour down to 500 F, then air cool.
Aging: The aging precipitation heat treatment is done at 350 F for 8 hours followed by air cooling. This produces the T6 temper.
Application Commonly used in the manufacture of heavy-duty structures requiring good corrosion resistance, truck and marine components, railroad cars, furniture, tank fittings, general structural and high pressure applications, wire products, pipelines, various toolings etc.
 
Alloy Chemical Component %≤
Si Fe Cu Mn Mg Cr Ni Zn Ti others Al
single total
6061 0.4- 0.8 0.7 0.15-0.4 0.15 0.8- 1.2 0.04-0.35 \ 0.25 0.15 0.05 0.15 remainder
6082 0.7- 1.3 0.5 0.1 0.4- 1.0 0.6- 1.2 0.25 \ 0.2 0.1 0.05 0.15 remainder
6063 0.2-
0.6
0.35 0.1 0.1 0.45-0.9 0.1 \ 0.1 0.1 0.05 0.15 remainder
Contact Ms. Margaret   Tel: 0086-0535-6501189

Factory Price of En Standard 3003/5005/5052/5083 /6061 Aluminum Alloy Sheet /Plate
Factory Price of En Standard 3003/5005/5052/5083 /6061 Aluminum Alloy Sheet /Plate
Factory Price of En Standard 3003/5005/5052/5083 /6061 Aluminum Alloy Sheet /Plate

Contact us if you need more details on Aluminum Alloy. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Aluminum Alloy PlateAluminum Plate. If these products fail to match your need, please contact us and we would like to provide relevant information.