5052 H32 Aluminum Panel Discount 4′*8′ Mill Finish Building Material Hardware for India Market

Basic Info

Model No.:  5052 H32

Product Description

Model NO.: 5052 H32 Alloy: 5052 Thickness: 0.5-300mm Trademark: BAODI Origin: China Color: Silver Temper: H32 Size: 1000*2000mm,1220*2440mm,1200*2400mm Specification: GB/T 3880-2006 HS Code: 76061250 5052 
 
Aluminum Balance
Chromium 0.15 - 0.35
Copper 0.1 max
Magnesium 2.2 - 2.8
Manganese 0.1 max
Remainder Each 0.05 max
Remainder Total 0.15 max
Silicon + Iron 0.45 max
Zinc 0.1 max

Size:thickness from 0.5mm-300mm
        width from 1000-1500mm
        length from 2000-6000mm
The size can be customized.
 
Principal Design Features:

This is a non-heat treatable alloy that is weldable. It is hardened by cold work. It has good forming characteristics and good corrosion resistance, including resistance to salt water.
Applications
Commonly used in the manufacture of hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, and appliances. Commonly used in sheet metal work and in sheet metal parts.

Machinability:

This alloy has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
Forming
AL 5052 is readily formed at room temperature. Successive cold working decreases the formability.
Welding
This alloy is readily welded by conventional methods. When filler rod is required it should be aluminum alloy 5356 as filler. Either tungsten or consumable electrode inert gas shielded arc welding is preferred method.

Heat Treatment:

AL 5052 cannot be hardened by means of heat treatment. It does harden due to cold working.
Forging
The alloy may be forged in the temperature range of 950 F down to 500 F.
Hot Working
Hot working, as with forging, may be done in the range of 950 F to 500 F.
Cold Working
The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
Annealing
Anneal at 650 F and air cool.
Hardening
Hardens only from cold working.
Other Physical Props
Electrical conductivity 33% of copper.
Other Mechanical Props
Shear strength for O temper is 18 ksi. For cold worked temper H 34 it is 21 ksi.
Physical Data
Density (lb / cu. in.)  0.097
Specific Gravity  2.68
Melting Point (Deg F)  1130
Modulus of Elasticity Tension  10.2
Modulus of Elasticity Torsion  3.8

Contact us if you need more details on Aluminum Panel. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Mill Finish Aluminum Panel、Building Material. If these products fail to match your need, please contact us and we would like to provide relevant information.

Product Categories : Other Decoration Materials

Email to this supplier
  • *Subject:
  • To:

  • *Messages:
    Your message must be between 20-8000 characters